acicular structure | 2.2.47 |
ageing | 2.1.34 |
air-hardening steel | 2.2.45 |
alloy | 2.2.22 |
alpha iron | 2.2.1 |
aluminizing | 2.1.5 |
annealing | 2.1.25 |
austempering | 2.1.15.2.1 |
austenite | 2.2.6 |
austenitic steel | 2.2.39 |
austenitizing | 2.1.6 |
austenitizing temperature | 2.1.6.1 |
auto-tempering | 2.1.26.6 |
bainite | 2.2.8 |
baking | 2.1.25.15 |
banded structure | 2.2.48 |
blank carburizing | 2.1.40.3 |
blank nitriding | 2.1.4.2 |
blueing | 2.1.9 |
boost-Diffuse carburizing | 2.1.40.4 |
boriding | 2.1.7 |
bright annealing | 2.1.25.11 |
burning | 2.1.18.7 |
carbon activity | 2.2.5 |
carbon mass transfer coefficient | 2.2.18 |
carbon potential | 2.2.33 |
carbon profile | 2.2.12 |
carbon restoration | 2.1.40.5 |
case depth | 2.1.40.2 |
case hardening | 2.1.40 |
cast iron | 2.2.59 |
cementite | 2.2.58 |
chromizing | 2.1.39 |
constituant | 2.2.49 |
continuous-cooling-transformation Diagram (CCT Diagram) | 2.1.27.2 |
cooling | 2.1.27 |
cooling conditions | 2.1.27.11 |
cooling curve | 2.1.27.3 |
cooling function | 2.1.27.12 |
cooling rate | 2.1.27.7 |
cooling schedule | 2.1.27.6 |
cooling time | 2.1.27.5 |
critical cooling rate | 2.1.27.4 |
critical diameter | 2.2.20 |
crystallinity | 2.2.19 |
decarburizing | 2.1.21 |
delta iron | 2.2.3 |
depth of decarburization | 2.1.21.1 |
depth of nitriding | 2.1.4.1 |
depth of transformation | 2.1.29 |
destabilization of retained austenite | 2.1.26.2 |
diffusion treatment | 2.1.14 |
diffusion zone | 2.1.31 |
direct hardening treatment | 2.1.15.9 |
direct quenching | 2.1.15.9 |
distortion | 2.2.17 |
double quench hardening treatment | 2.1.15.1 |
effective case depth after carburizing | 2.1.40.1 |
effective case depth after surface hardening | 2.1.16.1 |
endothermic atmosphere | 2.1.43 |
epsilon carbide | 2.2.4 |
equalization | 2.1.18.9 |
eutectoid transformation | 2.2.31 |
exothermic atmosphere | 2.1.42 |
ferrite | 2.2.57 |
ferritic steel | 2.2.38 |
floor to floor time | 2.1.1.2 |
full annealing | 2.1.25.9 |
gamma iron | 2.2.2 |
grain | 2.2.15 |
grain boundary | 2.2.13 |
grain coarsening | 2.1.25.6 |
grain growth | 2.2.35 |
grain refining | 2.1.22 |
grain size | 2.2.9 |
graphitic steel | 2.2.40 |
graphitizing | 2.1.10 |
hardenability | 2.2.32 |
heat treatment | 2.1.1 |
heating | 2.1.18 |
heating curve | 2.1.18.5 |
heating function | 2.1.18.13 |
heating rate | 2.1.18.12 |
heating schedule | 2.1.18.10 |
heating time | 2.1.18.11 |
heating-up time | 2.1.18.3 |
high-temperature thermomechanical treatment | 2.1.3.1 |
homogenizing | 2.1.25.2 |
hypereutectoid steel | 2.2.42 |
hypoeutectoid steel | 2.2.41 |
impulse hardening | 2.1.15.3 |
impulse heating | 2.1.18.1 |
incomplete quenching | 2.1.15.5 |
induction hardening (Surface hardening treatment) | 2.1.15.6 |
inter-critical annealing | 2.1.25.4 |
inter-critical treatment | 2.1.1.1 |
internal oxidation | 2.2.27 |
interrupted quenching | 2.1.15.7 |
interrupted quenching | 2.1.15.8 |
isoforming | 2.1.11 |
jominy test | 2.1.29.1 |
ledeburite | 2.2.23 |
ledeburitic steel | 2.2.43 |
limiting ruling section | 2.2.21 |
local hardening | 2.1.15.4 |
low load hardness | 2.2.51 |
low-temperature thermomechanical treatment | 2.1.3.2 |
maraging | 2.1.34.1 |
maraging steel | 2.2.44 |
martempering | 2.1.15.2 |
martensite | 2.2.24 |
mass effect | 2.2.10 |
maximum achievable hardness | 2.1.15.13 |
McQuaid-Ehn grain size | 2.2.28 |
medium | 2.1.32 |
microhardness | 2.2.26 |
nitriding | 2.1.4 |
nitrocarbunzing | 2.1.19 |
nitrogen profile | 2.2.11 |
normalizing | 2.1.20 |
normalizing forming | 2.1.12 |
operation | 2.1.1.3 |
overcarburizing | 2.2.29 |
overheating and oversoaking | 2.1.18.6 |
parent phase | 2.2.56 |
patenting | 2.1.28 |
pearlite | 2.2.30 |
phase | 2.2.55 |
precipitation hardening | 2.2.14 |
precipitation hardening traitement | 2.1.17 |
preheating | 2.1.18.2 |
quench hardened layer | 2.1.16 |
quench hardening treatment | 2.1.15 |
quenching capacity | 2.1.27.1 |
quenching temperature | 2.1.15.14 |
recalescence | 2.2.34 |
recovery | 2.1.25.1 |
recrystallizing | 2.1.25.10 |
retained austenite | 2.2.7 |
secondary hardening | 2.1.26.1 |
secondary martensit | 2.2.25 |
self-quenching | 2.1.15.10 |
sensitization | 2.2.36 |
sherardizing | 2.1.41 |
siliconizing | 2.1.30 |
soaking | 2.1.18.4 |
softening | 2.1.25.12 |
solid solution | 2.2.52 |
solution annealing | 2.1.25.8 |
solution treatment | 2.1.23 |
spheroidization | 2.2.50 |
spheroidizing | 2.1.25.7 |
stabilization of retained austenite | 2.1.33.1 |
stabilizing | 2.1.33 |
stabilizing annealing | 2.1.25.13 |
steel | 2.2.37 |
step quenching | 2.1.15.12 |
stress relief tempering | 2.1.26.4 |
stress relieving | 2.1.25.5 |
sub-critical annealing | 2.1.25.14 |
sub-zero treating | 2.1.24 |
sulphidizing | 2.1.35 |
temper embrittlement | 2.1.26.5 |
tempering | 2.1.26 |
tempering curve | 2.1.26.3 |
thermal cycle | 2.1.36 |
thermochemical treatment | 2.1.2 |
thermomechanical treatment | 2.1.3 |
through-hardening | 2.1.15.11 |
time-temperature-transformation Diagram (TTT Diagram) | 2.1.13 |
transformation range | 2.2.16 |
transformation temperature | 2.1.37 |
transformation temperature | 2.2.53 |
transformation temperature | 2.2.55 |
two stage nitriding | 2.1.4.3 |
umwandeln in der Perlitstufe | 2.1.25.3 |
vanadizing | 2.1.8 |
Widmannstaetten structure | 2.2.46 |